Fire Resistant Paint & High Temperature Paint

Organic Silicone Heat Resistant Paint 200℃/400℃/600℃

Widely used in blast furnace, hot blast furnace, internal and external wall, chimney, drying tunnel, exhaust pipe, high temperature heat pipe, heating furnace, heat exchanger and other non metal and metal surface high temperature corrosion protection. The
INQUIRY
Description
Product Formation
Be made of special heat resistant resin, high temperature resistant pigment, filler, additives and solvent.
 
Product Features
. Drying in normal temperature,good adhesion
. Excellent heat resistance and weather resistance, water resistance, chemical resistance
. Good mechanical properties
. No loss, no bubble, no cracking, no powder
 
 Using:
Widely used in blast furnace, hot blast furnace, internal and external wall, chimney, drying tunnel, exhaust pipe, high temperature heat pipe, heating furnace, heat exchanger and other non metal and metal surface high temperature corrosion protection. The surface temperature is less than 400℃
 
 Packing
Paint:18 kg/bucket 
 
Technical Data:
Color and appearance of paint film          Iron red, film formation
Viscosity (Stormer viscometer), KU          50-80
Dry film thickness, um                     40
Solids content,%                          50-60
Flashing point,℃                          33
Drying time (25℃), H                      surface dry 2h, hard dry≤24hrs
Drying (200 ℃)                           ≤ 0.5h
Adhesion (zoned method), class            ≤2
Impact strength, kg, CM                   ≥50
Bending strength, mm                     ≤5
Flexibility, mm                             1
Water resistance                          72 hrs
Heat resistance                           6 hrs
 
Double Coating Interval Time:
Temperature              5℃             25℃             40℃            
Shortest time             4h               2h                1h
Longest time                            no limited  
 
Surface Treatment:
Coating shall be clean objects surface dust, oil, welding slag, rust and old paint processing, steel surface sandblasting, shot peening to Sa2.5. Local repair surface require grinding to ST3 level. Construction is strictly prohibited into water.  
 
Auxiliary Paint :
Zinc silicate shop primer, zinc rich coating      
 
Construction Condition:
The temperature of the base material must be above the dew point above 3 degrees C, but must not be more than 60 degrees Celsius, the fog, rain, snow, wind and rain is strictly prohibited under the construction.
 
Construction Method:
Spraying: non air spraying or air spraying. High pressure non gas spraying.
Brush / roll coating: must achieve the specified dry film thickness.

 
+86 13725287956